Table 4 shows the tensile strength and elongation at break both HMw and LMw of chitosan-based films dried at room temperature (RT) and heat treated (HT). On the other hand, when films were heat-treated, both tensile strength and elongation at break increased by the effect of temperature for HMw chitosan-based films, regardless of glycerol content.