During pressing the temperature and the pressure are substantially increased. This means that even large voids can be dissolved in a very short time. If the pressure is large enough within the resin most enclosed gas should dissolve and SMC products ought to be com-pletely free from voids. It is well known that these items can have a relatively high void content. There are several reasons for this