This research is to study the physical properties of the ceiling tiles of gypsum and rice husk. By using the adhesives as a Interfaces in 5,10, and 15 percent of the quantity water, respectively. Handsome in the mold size 300 x 300 x 18 mm. Then tested the physical properties such as TIS 219-2552. Found that when mixed increase volume adhesives result a absorption. And moisture lower But the Density, Compressive strength and modulus of rupture more. Which the ratio adhesives 15 percent compressive strength and modulus of rupture through the standard TIS 219-2552 is 175.43 Newton and 2.75 MPa. Thereafter the gypsum mixed with rice husk in percent ratio 100:0, 95:5, 90:10, 85:15, and 80:20 by weight, respectively. Found that the ratio of ceiling tiles, gypsum with rice husk is the most appropriate at a 95:5, percentage. density is 0.0140 g/cm3. percent absorption 6.84, moisture at 2 and 24 hours was 17 percent and 20 percent, the compressive strength and modulus of rupture through the Standard TIS 219-2552 is 175.63 Newton and 2.75 MPa. The rice husk can be developed to production as ceiling tiles for the construction in the future.