Our results demonstrated that pure stereocomplex can be
achieved by a low temperature approach, i.e. processing at
temperatures much lower than those adopted in conventional melt
blending, using high-molecular-weight PLA that are difficult to
form stereocomplex using conventional melt blending and solution
casting methods.