Since there is essentially no amorphous phase in the single crystalline polymer, it was proposed that this process may also reflect chain motions due to structural defects in the crystalline phase. As demonstrated later, this dielectric re-laxation includes a significant contribution from domain wall and polar defect motions in the normal ferroelectric P(VDF-TrFE) copolymer.