Figure 1. Typical measured recalescence curves and as-solidifiedmicros การแปล - Figure 1. Typical measured recalescence curves and as-solidifiedmicros ไทย วิธีการพูด

Figure 1. Typical measured recalesc

Figure 1. Typical measured recalescence curves and as-solidified
microstructures, (a, c) and (b, d) correspond to DT < D T* and
DT > DT*, respectively. (a) and (b) are the measured recalescence
profiles with the above-mentioned two-color pyrometer, where Tdl
, Tp
and Tds
are liquidus temperature of the d phase, equilibrium peritectic
reaction plateau temperature and solidus temperature of d phase,
respectively. The left insert corresponds to the solidification and the
right one corresponds to the d!c transformation. (Note: to observe
the full thermal histories of samples in situ, the measured temperature
profiles were taken from the samples without quenching treatment.) (c)
Typical microstructure with DT < DT* etched with Oberhoffer’s
reagent (30 g FeCl3, 1 g CuCl2, 0.5 g SnCl2, 50 ml HCl, 500 ml ethyl
alcohol, 500 ml distilled water), showing peritectic solidification
characteristics; the primary d dendrites (dark) are enveloped by the
peritectic c phase (white). (d) Typical microstructure with DT > D T*
etched with 3 wt.% Nital’s reagent to reveal the grain boundaries and
the morphologies of second-phase particles; inserts are the TEM bright
field images of the RT microstructure, the left is the morphology of the
matrix and the right is the morphology of the second-phase particles
0/5000
จาก: -
เป็น: -
ผลลัพธ์ (ไทย) 1: [สำเนา]
คัดลอก!
รูปที่ 1 ปกติวัดเส้นโค้ง recalescence และ หล่อเป็นmicrostructures, (a, c) และ (b, d) กับ DT < T D * และDT > DT * ตามลำดับ (ก) และ (ข) recalescence วัดโพรไฟล์กับ pyrometer สองสีดังกล่าว ซึ่ง Tdl, Tpและ Tdsมีอุณหภูมิ liquidus เฟส d, peritectic สมดุลปฏิกิริยาที่ราบสูงอุณหภูมิและอุณหภูมิ solidus เฟส dตามลำดับ แทรกซ้ายตรงกับที่ solidification และขวาหนึ่งตรงไป d ! c แปลง (หมายเหตุ: สังเกตหากความร้อนเต็มรูปแบบของตัวอย่างใน situ วัดอุณหภูมิโพรไฟล์ได้นำจากตัวอย่างโดยไม่ต้องชุบรักษา) (c)ต่อโครงสร้างจุลภาคโดยทั่วไปกับ DT < DT * แกะสลักกับของ Oberhofferรีเอเจนต์ (30 g FeCl3, 1 g CuCl2, 0.5 g SnCl2, 50 ml HCl เอทิลขนาด 500 มล.แอลกอฮอล์ น้ำกลั่นขนาด 500 มล.), แสดง peritectic solidificationลักษณะ เป็นขัดหลัก dendrites d (มืด) โดยperitectic c ระยะ (สีขาว) (d) ต่อโครงสร้างจุลภาคโดยทั่วไปกับ DT > D T *แกะสลัก ด้วยรีเอเจนต์ของ Nital 3 wt.% แพร่งขอบเม็ด และmorphologies ของเฟสสองอนุภาค แทรกเป็นยการสดใสต่อโครงสร้างจุลภาค RT ฟิลด์ภาพซ้ายเป็นสัณฐานวิทยาของการเมตริกซ์และด้านขวาเป็นสัณฐานวิทยาของอนุภาคที่สองเฟส
การแปล กรุณารอสักครู่..
ผลลัพธ์ (ไทย) 2:[สำเนา]
คัดลอก!
Figure 1. Typical measured recalescence curves and as-solidified
microstructures, (a, c) and (b, d) correspond to DT < D T* and
DT > DT*, respectively. (a) and (b) are the measured recalescence
profiles with the above-mentioned two-color pyrometer, where Tdl
, Tp
and Tds
are liquidus temperature of the d phase, equilibrium peritectic
reaction plateau temperature and solidus temperature of d phase,
respectively. The left insert corresponds to the solidification and the
right one corresponds to the d!c transformation. (Note: to observe
the full thermal histories of samples in situ, the measured temperature
profiles were taken from the samples without quenching treatment.) (c)
Typical microstructure with DT < DT* etched with Oberhoffer’s
reagent (30 g FeCl3, 1 g CuCl2, 0.5 g SnCl2, 50 ml HCl, 500 ml ethyl
alcohol, 500 ml distilled water), showing peritectic solidification
characteristics; the primary d dendrites (dark) are enveloped by the
peritectic c phase (white). (d) Typical microstructure with DT > D T*
etched with 3 wt.% Nital’s reagent to reveal the grain boundaries and
the morphologies of second-phase particles; inserts are the TEM bright
field images of the RT microstructure, the left is the morphology of the
matrix and the right is the morphology of the second-phase particles
การแปล กรุณารอสักครู่..
ผลลัพธ์ (ไทย) 3:[สำเนา]
คัดลอก!
รูปที่ 1 โดยทั่วไปวัด recalescence เส้นโค้งและเป็นโครงสร้างแข็ง
( C ) , ( B , D ) สอดคล้องกับ DT < d T *
DT > DT * ตามลำดับ ( ก ) และ ( ข ) เป็นวัด recalescence
โปรไฟล์กับวัดอุณหภูมิสองสีดังกล่าวที่ TDL


TP และ TDS อุณหภูมิลิควิดัสของ D เฟสสมดุลเพอริเทคติก
อุณหภูมิสูงและอุณหภูมิของปฏิกิริยาโซลิดัส
D เฟส ตามลำดับ แทรกซ้ายสัมพันธ์กับการแข็งตัวและ
ถูกต้องสอดคล้องกับ D C การเปลี่ยนแปลง ( หมายเหตุ : สังเกต
ประวัติเต็มของความร้อนตัวอย่างใน situ , วัดอุณหภูมิ
โปรไฟล์ นำมาจากตัวอย่างโดยไม่ดับการรักษา ( C )
)โดยทั่วไปโครงสร้างจุลภาคกับ DT < DT * กัดด้วย oberhoffer เป็น
3 ( 30 g FeCl3 , 1 กรัม cucl2 0.5 กรัม sncl2 50 ml HCL 500 มล. -
เหล้า 500 มล. น้ำกลั่น ) แสดงลักษณะเป็นก้อนแข็ง
เพอริเทคติก ; หลัก D กุยช่าย ( มืด ) ที่คลุมด้วย
( C เฟสเพอริเทคติกสีขาว ) ( D ) โดยทั่วไปโครงสร้างจุลภาคกับ DT > D t *
สลัก 3 โดยน้ำหนัก% nital เป็นรีเอเจนต์เพื่อแสดงขอบเขตและลักษณะของเม็ด
อนุภาคระยะที่สอง ; แทรกอยู่เต็มสนามสดใส
รูปของ RT โครงสร้างจุลภาค ด้านซ้ายเป็นสัณฐานของ
เมทริกซ์และขวาเป็นสัณฐานของอนุภาคระยะที่ 2
การแปล กรุณารอสักครู่..
 
ภาษาอื่น ๆ
การสนับสนุนเครื่องมือแปลภาษา: กรีก, กันนาดา, กาลิเชียน, คลิงออน, คอร์สิกา, คาซัค, คาตาลัน, คินยารวันดา, คีร์กิซ, คุชราต, จอร์เจีย, จีน, จีนดั้งเดิม, ชวา, ชิเชวา, ซามัว, ซีบัวโน, ซุนดา, ซูลู, ญี่ปุ่น, ดัตช์, ตรวจหาภาษา, ตุรกี, ทมิฬ, ทาจิก, ทาทาร์, นอร์เวย์, บอสเนีย, บัลแกเรีย, บาสก์, ปัญจาป, ฝรั่งเศส, พาชตู, ฟริเชียน, ฟินแลนด์, ฟิลิปปินส์, ภาษาอินโดนีเซี, มองโกเลีย, มัลทีส, มาซีโดเนีย, มาราฐี, มาลากาซี, มาลายาลัม, มาเลย์, ม้ง, ยิดดิช, ยูเครน, รัสเซีย, ละติน, ลักเซมเบิร์ก, ลัตเวีย, ลาว, ลิทัวเนีย, สวาฮิลี, สวีเดน, สิงหล, สินธี, สเปน, สโลวัก, สโลวีเนีย, อังกฤษ, อัมฮาริก, อาร์เซอร์ไบจัน, อาร์เมเนีย, อาหรับ, อิกโบ, อิตาลี, อุยกูร์, อุสเบกิสถาน, อูรดู, ฮังการี, ฮัวซา, ฮาวาย, ฮินดี, ฮีบรู, เกลิกสกอต, เกาหลี, เขมร, เคิร์ด, เช็ก, เซอร์เบียน, เซโซโท, เดนมาร์ก, เตลูกู, เติร์กเมน, เนปาล, เบงกอล, เบลารุส, เปอร์เซีย, เมารี, เมียนมา (พม่า), เยอรมัน, เวลส์, เวียดนาม, เอสเปอแรนโต, เอสโทเนีย, เฮติครีโอล, แอฟริกา, แอลเบเนีย, โคซา, โครเอเชีย, โชนา, โซมาลี, โปรตุเกส, โปแลนด์, โยรูบา, โรมาเนีย, โอเดีย (โอริยา), ไทย, ไอซ์แลนด์, ไอร์แลนด์, การแปลภาษา.

Copyright ©2024 I Love Translation. All reserved.

E-mail: