Here, we see that a stoichiometric ratio of Fe3+ to Fe2+ equal to 2:1 in the solid
phase is best achieved at room temperatures, which give the largest window of pH values, from 10.0 to 13.0, where a near perfect 2:1 stoichiometric solid may be produced