Cellulose nanocrystals prepared via formic acid hydrolysis followed
by TEMPO-mediated oxidation.
Cellulose nanocrystals (CNCs) as a renewable and biodegradable nanomaterial have wide application
value. In this work, CNCs were extracted from bleached chemical pulp using two stages of isolation
(i.e. formic acid (FA) hydrolysis and 2,2,6,6-tetramethyl-piperidine-1-oxyl (TEMPO) mediated oxidation)
under mild conditions. In the first stage, FA was used to remove hemicellulose, swell cellulose fibers,
and release CNCs. The FA could be readily recovered and reused. In the second stage, the CNCs isolated
by FA were further modified by TEMPO-mediated oxidation to increase the surface charge of CNCs. It
was found that the modified CNCs with more ordered crystal structure and higher surface charge had
better redispersibility and higher viscosity in aqueous phase. Therefore, the modified CNCs could be more
effective when used as rheology modifier in the fields of water based coating, paint, food etc.
เซลลูโลส nanocrystals เตรียมผ่านกรดย่อยสลายตามโดยจังหวะโดยการเกิดออกซิเดชันเซลลูโลส ( nanocrystals CNCs ) เป็นพลังงานทดแทนและย่อยสลายได้ทางชีวภาพวัสดุนาโนมีโปรแกรมหลากหลายค่า ในงานนี้ , CNCs สกัดจากเยื่อเคมีฟอกขาวที่ใช้สองขั้นตอนของการแยก( เช่นกรด ( FA ) และการย่อย 2,2,6,6-tetramethyl-piperidine-1-oxyl ( จังหวะ ) ( ออกซิเดชัน )ภายใต้ภาวะที่ไม่รุนแรง ในขั้นตอนแรก ฟ้าถูกใช้เพื่อเอาเส้นใยเซลลูโลส เฮมิเซลลูโลส , บวม ,และปล่อย CNCs . เอฟเอ น่าจะพร้อมกลับ 2 . ในขั้นตอนที่สอง , CNCs แยกโดย เอฟเอ ได้แก้ไขโดยการเพิ่มจังหวะโดยประจุพื้นผิวของ CNCs . มันพบว่า การสั่งให้ CNCs กับโครงสร้างผลึกและค่าธรรมเนียมที่สูง มีพื้นผิวredispersibility ดีกว่าและความหนืดสูงกว่าในน้ำขั้นตอน ดังนั้น การปรับเปลี่ยน CNCs ต้องมีประสิทธิภาพเมื่อใช้เป็นสมบัติที่ในเขตของน้ำเคลือบ ตามสี , อาหาร ฯลฯ