The fracture on a turbine blade of a turbojet engine has been investigated to see the cause of crack initiation. The fractured turbine blade did not seem to have suffered any damages by foreign objects. The turbine blade had initially cracked by a fatigue mechanism over a period of time and then fractured by the overload at the last moment.