Fig. 8. TGA curve in oxygen atmosphere of the SiC. indicating that only a very small percentage of SiC is oxidized. At 1300 C the mass of SiC remains at 93.5 %. These results indicate that the synthesized SiC is stable losing only 6.5% of its weight.