2. ExperimentalThe substrates used in this study were slip cast siliconized SiC having the properties listed in Table 1. The material was considered as relatively pure with impurities in the p.p.m. level, as shown in Table 2, and had a very wide range of grain sizes going from sub-micrometers to hundreds of micrometers.