The crystalline nature of the film samples was evaluated using XRD
analysis and the resulting XRD patterns of the carrageenan and
carrageenan-based nanocomposite films are shown in Fig. 3.
As shown
in Fig. 3a, the first broad band and the second minor peak observed
commonly at 2θ around 20° and 28° may be attributed to the carrageenan
base film (Rhimet al., 2013).
Except that, no characteristic diffraction
peaks were observed in the neat carrageenan and carrageenan/clay
mineral films. However, carrageenan/AgNP and carrageenan/AgNP/
clay mineral films exhibited similar diffraction profiles and diffraction
peaks at 2θ of 38.2° and 44.4°, which can be attributed to the (111)
and (200) crystallographic planes of face-centered cubic (fcc) silver
crystals, respectively (Pandey et al., 2012). Unexpectedly, both AgNPincluded
films showed unexpected intense peak at 2θ of 32.31°, which
corresponds to the diffraction peak of Na2O2 (Hill et al., 1997).
Presumably
the Na2O2 originates from sodium citrate used for the reduction of
AgNO3.
The carrageenan/AgNP film exhibited more intense peaks than
the carrageenan/AgNP/clay mineral film.
The approximate mean crystallite
size (D) of the AgNPs in the composite films, calculated using
the Scherrer equation, ranged from23.7 to 35.6 nm, which was comparable
to that of 21.3 to 23.8 nm of agar/AgNP composite films (Rhim
et al., 2013).
However, the peak positions of the carrageenan/clay mineral
composite and carrageenan/AgNP/clay mineral composite films
The crystalline nature of the film samples was evaluated using XRDanalysis and the resulting XRD patterns of the carrageenan andcarrageenan-based nanocomposite films are shown in Fig. 3. As shownin Fig. 3a, the first broad band and the second minor peak observedcommonly at 2θ around 20° and 28° may be attributed to the carrageenanbase film (Rhimet al., 2013). Except that, no characteristic diffractionpeaks were observed in the neat carrageenan and carrageenan/claymineral films. However, carrageenan/AgNP and carrageenan/AgNP/clay mineral films exhibited similar diffraction profiles and diffractionpeaks at 2θ of 38.2° and 44.4°, which can be attributed to the (111)and (200) crystallographic planes of face-centered cubic (fcc) silvercrystals, respectively (Pandey et al., 2012). Unexpectedly, both AgNPincludedfilms showed unexpected intense peak at 2θ of 32.31°, whichcorresponds to the diffraction peak of Na2O2 (Hill et al., 1997). Presumablythe Na2O2 originates from sodium citrate used for the reduction ofAgNO3. The carrageenan/AgNP film exhibited more intense peaks thanthe carrageenan/AgNP/clay mineral film. The approximate mean crystallitesize (D) of the AgNPs in the composite films, calculated usingthe Scherrer equation, ranged from23.7 to 35.6 nm, which was comparableto that of 21.3 to 23.8 nm of agar/AgNP composite films (Rhimet al., 2013). However, the peak positions of the carrageenan/clay mineralcomposite and carrageenan/AgNP/clay mineral composite films
การแปล กรุณารอสักครู่..
ธรรมชาติ ( ภาพยนตร์ตัวอย่างทดลองใช้ การวิเคราะห์ และผลวิเคราะห์รูปแบบของคารา คาราและนาโนคอมโพสิตเตอร์
ตามภาพยนตร์ที่แสดงในรูปที่ 3
ในรูปเป็น 3A , แรกที่สองและบรอดแบนด์สูงสุดรองสังเกต
ปกติที่ 2 θประมาณ 20 องศาและ 28 องศา อาจ เนื่องจากแนน
ฐานฟิล์ม ( rhimet al . , 2013 ) .
ยกเว้นว่าไม่มียอดการเลี้ยวเบน
ลักษณะพบในคาราจีแนนเรียบร้อยและคาราจีแนน / ดิน
ภาพยนตร์แร่ อย่างไรก็ตาม agnp และคาราจีแนนแนน / / /
agnp แร่ดินเบนภาพยนตร์มีโปรไฟล์ที่คล้ายกันยอดการเลี้ยวเบน
ที่ 2 θ 38.2 ° และของทุกองศา ซึ่งสามารถนำมาประกอบกับ ( 111 )
( 200 ) และระนาบของผลึกของลูกบาศก์ ( FCC ) ผลึกสีเงิน
,ตามลำดับ ( เดย์ et al . , 2012 ) โดยไม่คาดคิด ทั้ง agnpincluded
ภาพยนตร์ที่รุนแรงพบสูงสุดที่ 2 θของ 32.31 °ซึ่ง
สอดคล้องกับจุดสูงสุดของ na2o2 การเลี้ยวเบน ( เนินเขา et al . , 1997 ) .
na2o2 สันนิษฐานมาจากโซเดียมซิเตรตที่ใช้สำหรับการลดลงของ
agno3 .
/ agnp คารามียอดภาพยนตร์ที่รุนแรงมากขึ้นกว่า
/ ฟิล์ม / แร่ดินเหนียว agnp คารา .
การประมาณหมายถึงผลึก
ขนาด ( D ) ของ agnps ในฟิล์มคอมโพสิต คำนวณโดยใช้สมการมีค่า
เชเรอร์ , from23.7 ถึง 35.6 nm ซึ่งเปรียบ
ที่ 21.3 ถึง 23.8 nm ของวุ้น / agnp ฟิล์ม ( rhim
et al . , 2013 )
อย่างไรก็ตาม ตำแหน่งสูงสุดของคาราจีแนน / ดินเหนียว ผสมแร่
และคาราจีแนน / agnp / ฟิล์มแร่ดินเหนียว
การแปล กรุณารอสักครู่..