In the tests cylindrical bars with 32 mm diameter
were taken as
samples (composition of AISI 1050 steel are given in Table 1 ) from
the AISI 1050 steel. The samples were wait at 860 C temperatures
that on 40 C of the Ac3 temperature, for 30 min and were applied
to normalization annealing at placid air cooling media