The WVUR5 of agar films decreased from 227.3±12.5% for the neat agar film as clay content increased. This result indicates that water vapor sensitivity property of the agar film is improved through nancomposite formation with the nanoclay.
The WVUR5 of agar films decreased from 227.3±12.5%for the neat agar film as clay content increased. This result indicatesthat water vapor sensitivity property of the agar film isimproved through nancomposite formation with the nanoclay.