A microwave assisted chemical preci

A microwave assisted chemical precipitation method has been employed for the synthesis of nano zinc
oxide rods by reacting zinc nitrate and potassium hydroxide. The amount of potassium hydroxide was
adjusted for three different pHs to achieve ZnO nano rods with varying aspect ratio. The mechanism of
growth of nano rods is explained briefly. The average crystallite size of the as synthesized samples was
analyzed by means of powder XRD pattern and estimated to vary from 25.6 nm to 43.1 nm.
The existence of rods was confirmed using scanning electron microscopy (SEM). The samples were
also analyzed using FT-IR. The optical properties of the samples were also studied by means of UV–
visible spectra and Room Temperature Photo Luminescence studies. The band gap of the samples was
determined from the DRS spectrum. A strong near band emission peaks due to surface defects are
observed in the PL spectrum.

ผลลัพธ์ (ไทย) 3:

มีไมโครเวฟวิธีตกตะกอนทางเคมีได้ถูกใช้ในการสังเคราะห์นาโนสังกะสีออกไซด์ สังกะสีแท่ง โดยปฏิกิริยา
ไนเตรตโพแทสเซียมไฮดรอกไซด์ ปริมาณของโพแทสเซียมไฮดรอกไซด์เป็น
ปรับสาม PHS ที่แตกต่างกันเพื่อให้บรรลุซิงค์ออกไซด์นาโนแท่งกับค่าอัตราส่วน กลไกของการเจริญเติบโตของแท่งนาโน
อธิบายสั้น ๆค่าเฉลี่ยของขนาดผลึกที่สังเคราะห์จำนวน
โดยใช้วิธีการวิเคราะห์แบบผง และประมาณว่าแตกต่างจาก 25.6 nm ถึง 43.1 nm .
การดำรงอยู่ของแท่งก็ยืนยันด้วยกล้องจุลทรรศน์อิเล็กตรอนแบบส่องกราด ( SEM ) จำนวน
ยังวิเคราะห์โดยใช้เทคนิค FT-IR . คุณสมบัติทางแสงของตัวอย่างที่ศึกษาโดยวิธีการ
- ยูวีสเปกตรัมที่มองเห็นแสงและอุณหภูมิห้องภาพการศึกษา ช่องว่างแถบของจำนวน
กำหนดจาก DRS สเปกตรัม แข็งแรง ใกล้วงปล่อยยอดเพราะข้อบกพร่องที่พบในผิวจะ
คุณสเปกตรัม