Porous layers were made using p-type GaAs(100) substrates
doped with Zn hole concentration 1018 cm3 and
InP(100) wafers doped with 1016 cm3 S. The samples were
degreased with acetone, propanol and methanol and extensively
rinsed with deionized water and were then blown