Due to these reasons the chemical routes of preparation have emerged as very popular synthesis tools
for nano particles of spinel ferrites. Among the various available preparation methods, to obtain nano
crystalline ferrite particles, viz hydrothermal synthesis [1-4], coprecipitation [5-9], sol-gel [10-13],
spraydrying [14], solid-state, microemulsion processes [15-17], and mechanical alloying [18-21],
coprecipitation method is chosen in the present work for preparing Co-Cu mixed ferrites. As it is well
known, co-precipitation is an economical way to produce homogenous nano ferrites. As prepared CobaltCopper
ferrite samples are sintered at 600 C and are subjected to X-ray diffraction. The FT-IR spectra of
these samples are recorded and the crystalline structure of the composite nano particles is characterized
by Transmission Electron Microscope (TEM).
เนื่องจากสาเหตุเหล่านี้ เส้นทางเคมีเตรียมได้เกิดเป็นเครื่องมือสังเคราะห์นิยมมากสำหรับอนุภาคนาโนของ spinel ferrites ระหว่างเตรียมหาวิธีการต่าง ๆ รับนาโนอนุภาคผลึก ferrite, viz hydrothermal สังเคราะห์ [1-4] coprecipitation [5-9], โซลเจ [10-13],spraydrying [14], โซลิดสเตต microemulsion กระบวน [15-17], และเครื่องกลลเท่านั้น [18-21],coprecipitation วิธีที่งานปัจจุบันเตรียมผสม ferrites Cu Co ก็ดีรู้จัก ฝนร่วมเป็นวิธีประหยัดการผลิตนาโนให้ ferrites เป็น CobaltCopper ที่เตรียมไว้ตัวอย่าง ferrite จะเผาที่ 600 C แล้วอยู่ภายใต้การเอ็กซ์เรย์การเลี้ยวเบน แรมสเป็คตรา FT-IR ของตัวอย่างเหล่านี้จะถูกบันทึก และลักษณะโครงสร้างผลึกของอนุภาคนาโนคอมโพสิตโดยการส่งผ่านอิเล็กตรอนกล้องจุลทรรศน์ (ยการ)