Composite films of polypropylene (P

Composite films of polypropylene (PP) and modified calcium carbonate (CaCO3) were prepared in a twin screw extruder with
particle content varying from 0.5, 1.0, and 1.5 phr. The CaCO3 surface was modified by palmitic acid (PA) at 1, 3, and 5 %wt.
The modified CaCO3 surface was characterized by FTIR and XRD to indicate that the modifier is combined on the CaCO3
surface. The results showed that optimum of PA attached to that CaCO3 surface was 5 %wt. The influence of modified CaCO3
with and without PA of PP film on the mechanical (tensile strength, Young’s modulus and elongation at break), barrier (OP),
thermal (DMTA, DSC), physical (XRD, SEM and OM) properties were studied. The results observed that incorporation of
modified CaCO3 0.5 phr into PP film showed more dispersion than PP with CaCO3. Furthermore, the addition modified CaCO3
increased tensile strength, Young’s modulus, oxygen permeability and melting point from 22.10 MPa, 984.21 MPa, 3.22

ผลลัพธ์ (ไทย) 1:

คอมโพสิตฟิล์มโพรพิลีน (PP) และแก้ไขแคลเซียมคาร์บอเนต (CaCO3) วจัดในสกรูคู่กับเนื้อหาอนุภาคที่แตกต่างจาก 0.5, 1.0, 1.5 และ phr. แก้ไขเมื่อ CaCO3 พื้นผิว ด้วยกรด palmitic (PA) ที่ 1, 3 และ 5% wtแก้ไขพื้นผิว CaCO3 ลักษณะพิเศษ โดย FTIR และ XRD เพื่อบ่งชี้ว่า การปรับปรุงจะถูกรวมบน CaCO3พื้นผิว ผลการศึกษาพบที่ที่เหมาะสมของ PA ที่แนบกับพื้นผิวที่ CaCO3 เป็น 5% wt อิทธิพลของ CaCO3 แก้ไขมี และไม่ มี PA ของ PP ฟิล์มบนเครื่องกล (แรงดึง โมดูลัสของยัง และยืดที่), อุปสรรค (OP),ความร้อน (DMTA, DSC), มีศึกษาคุณสมบัติทางกายภาพ (XRD, SEM และ OM) ผลการสังเกตที่รวมตัวกันของแก้ไข CaCO3 phr 0.5 ลงในฟิล์ม PP พบกระจายมากขึ้นกว่า PP กับ CaCO3 นอกจากนี้ การเพิ่มแก้ไข CaCO3เพิ่มความแข็งแรง โมดูลัสของหนุ่ม ออกซิเจนซึมผ่าน และจุดหลอมเหลวจาก 22.10 MPa, 984.21 MPa, 3.22