This special project was aimed to study on concrete behavior in terms of compressive strength, moisture content, unit weight and proportion of coarse aggregate. In this study, two (110x110x30 cm3) specimens were prepared for testing. One was cure by ponding method. The other was cured by covering with plastic film. Next, at 28 day curing, twenty concrete samples with 5 centimetre diameter at 30 centimetre depth were cored from each specimens. For each specimen. Fifteen samples were testd for determining compressive strength, moisture content, unit weight and proportion of coarse aggregate. The remaining five samples were tested for finding absorption and unit weight. It was found that compressive strength reversely varies to absorption and to porosity. In addition, it can be conclued that concrete cured by ponding method influences the development of concrete strength within the range of fifteen-centimetre depth from surface.