With further increasing of Caconten

With further increasing of Ca
content (x = 0.04), the orthorhombic to tetragonal phase transition
cannot be observed above room temperature. It is interesting
to note that phase transition temperature TO–T decrease obviously,
and the Curie temperature TC for each sample is above
60 ◦C. This result indicates that Ca addition does not strongly
affect the TC, but pushes the TO–T to lower temperatures in
BCST system.4,20 On the other hand, the dielectric constants are
found to be on the order of 5200, 5800, 6900 and 6300 for BCST
ceramics at x = 0.01, x = 0.02, x = 0.03 and x = 0.04, respectively. The dielectric loss is found to be on the order of 0.021, 0.018, 0.015 and 0.016 for the BCST ceramics at x = 0.01, x = 0.02, x = 0.03 and x = 0.04, respectively. The BCST ceramic at x = 0.03 is found to exhibit a high dielectric constant of 6900 and low dielectric loss of 0.015 at room temperature. The values show suitability of the composition for Y5V type of multilayer chip capacitors.

ผลลัพธ์ (ไทย) 3:

เพิ่มเติมด้วยการเพิ่ม CA
เนื้อหา ( X = 0.04 ) , ออร์โทรอมบิก เพื่อการเปลี่ยนเฟสเตตระโกนอล
ไม่สามารถสังเกตเหนืออุณหภูมิห้อง เป็นที่น่าสนใจที่จะทราบว่าอุณหภูมิการเปลี่ยนเฟส

- T จะลดลงอย่างชัดเจนและ TC , อุณหภูมิคูรีสำหรับแต่ละตัวอย่างข้างบน
60 ◦ C . ผลนี้บ่งชี้ว่า CA ซึ่งไม่ขอ
ต่อ TC ,แต่ดันไป– T เพื่อลดอุณหภูมิใน
ระบบ BCST 4,20 บนมืออื่น ๆ , ค่าคงที่ไดอิเล็กตริกเป็น
พบเป็นลำดับที่ 5 , 200 , 300 , 900 , และสำหรับเครื่อง 6300 BCST
ที่ x = x = 0.01 , 0.02 , 0.03 และ x = x = 0.04 ตามลำดับ การสูญเสียไดอิเล็กตริก พบอยู่ในลำดับของ 0.021 และ 0.016 , 0.018 3 สำหรับ BCST เซรามิกที่ x = x = 0.01 , 0.02 , 0.03 และ x = x = 0.04 ,ตามลำดับ โดย BCST เซรามิกที่ x = 0.03 พบเพื่อแสดงค่าไดอิเล็กทริกสูงและต่ำการสูญเสียไดอิเล็กทริกของ 3 , 900 ที่อุณหภูมิห้อง ค่าแสดงความเหมาะสมขององค์ประกอบ y5v ประเภทของชิป Multilayer Capacitors .