X-ray powder diffraction analysis was performed using Xpert MPD (phillip, Belgium), operating at 40 mA and 45 kV with Cu. Freeze-dried micro-scale materials were acquired at an angu- lar range of 2θ from 41 to 991 with step-size of 0.051. Counting time was 2 s per step.