the XRD patterns of the samples obtained in the present work exhibit broad Bragg reflections, suggesting the presence of crystals with small sizes, which was in agreement with the SEM and TEM results. From Fig. 1(f), it could be seen that the peak of the samples B exhibited little intensity change after five cycles, indicating that their microcrystalline form was well remained.