3.2 Structural characterizationThe

3.2 Structural characterization
The XRD results of the La0.7Sr0.3MnO3 nanoparticles prepared
by thermal decomposition of the precursor A and B
at 800◦C for 6 h are shown in Fig. 2. Both samples show
a main phase of LSMO, but the sample prepared using precursor
B contains a large amount of impurities La(OH)3 and
SrCO3 (Fig. 2(b)). In this study, we therefore focus on the
LSMO nanoparticles prepared using the precursor A. Figure
3 shows the XRD results of the samples prepared by
thermal decomposition of the precursor A in air at 600, 700,
800, 900, and 1000◦C for 6 hours. The presence of impurities
phases such as SrCO3 (JCPD no. 05-0418), La2O2CO3
(JCPD no. 37-0804) and La(OH)3 (JCPD no. 36-1481)
was observed in the samples thermally decomposed below
800◦C, while above 800◦C the samples exhibited a pure
phase of LSMO. The transformation of the crystal structure
from cubic to rhombohedral occurred at and above 900◦C.

ผลลัพธ์ (ไทย) 3:

3.2 การศึกษาโครงสร้าง
วิเคราะห์ผลของอนุภาคนาโนที่เตรียมโดยการย่อยสลาย la0.7sr0.3mno3
ความร้อนของสาร A และ B
ที่ 800 ◦ C 6 H จะแสดงในรูปที่ 2 ทั้งสองตัวอย่างแสดง
เฟสหลักของ lsmo แต่ตัวอย่างที่เตรียมโดยใช้สารตั้งต้น :
b มีปริมาณของสิ่งเจือปนลา ( OH ) 3
srco3 ( รูปที่ 2 ( ข ) ) ในการศึกษานี้ ดังนั้นเราจึงมุ่งเน้น
lsmo นาโนที่เตรียมโดยใช้สารตั้งต้น . รูป
3 แสดงผลลัพธ์ของตัวอย่างที่เตรียมโดย XRD
สลายความร้อนของสารตั้งต้นในอากาศที่อุณหภูมิ 600 , 700 ,
800 , 900 และ 1000 ◦ C เป็นเวลา 6 ชั่วโมง การปรากฏตัวของสิ่งสกปรก
ขั้นตอนเช่น srco3 ( jcpd ไม่ 05-0418 ) la2o2co3
( jcpd ไม่ 37-0804 ) และลา ( OH ) 3 ( jcpd ไม่ 36-1481 )
) ในตัวอย่างด้านล่าง ซึ่งย่อยสลาย◦
800 Cในขณะที่ข้างต้น 800 ◦ C ตัวอย่างมีเฟสบริสุทธิ์ของ lsmo
. การเปลี่ยนแปลงของโครงสร้างคริสตัล
จากลูกบาศก์ที่จะเกิดขึ้นมากกว่าปกติและเหนือ 900 ◦ C