The TEManalysis confirmed
the formation of spherical particles at lowmicrowave power; however the morphology of the particles changed
to mesoporous needle and rod-like structure upon exposing the reaction mixture to higher microwave power
and longer retention time inside the microwave. The in-vitro ion dissolution behavior of the as synthesized hydroxyapatite
was studied by determining the amount of Ca2+ ion released in SBF solution.