The diminution of the
aggregation effect of Li+ ions on the glass structure due to the decrease in Li+ concentration, the larger
molecule weights of the substitutes, the mixed-alkali and depressing effects as well the slower mobility of
substitute ions mainly contribute to the initial changes in Tg, density and chemical durability of the LIP glasses respectively