Powder X-ray diffraction (XRD, PANa

Powder X-ray diffraction (XRD, PANalytical B.V., X′Pert Pro MPS PW3040/60) patterns of the samples were recorded in the scanning range of 5–80° at room temperature of 25°C. The morphologies, dimensions, elemental composition, and crystallinity of the nanopowders were examined by scanning electron microscopy (SEM, Hitachi, S-4800), energy dispersive X-ray spectroscopy (EDS) attached to the SEM, transmission electron microscopy (TEM), and high-resolution TEM (JEOL, JEM-2010HR), respectively. Samples for TEM observation were prepared by dispersing in ethanol. Differential scanning calorimetry (DSC, Netzsch-Bruker, STA449F3Jupiter-TENSOR27) experiments were performed using a DuPont differential thermal analyzer under atmosphere flow in the range of 25–120°C with a heating rate of 5 K min−1, and in the measure procedure heating process alternates with cooling process. The valance state of the as-obtained V 1 −

ผลลัพธ์ (ไทย) 1:

ผง x-เรย์เลนส์ (XRD, BV panalytical, x'pert โปร mps pw3040/60) รูปแบบของตัวอย่างที่ถูกบันทึกไว้ในช่วงการสแกนของ 5-80 °ที่อุณหภูมิห้องจาก 25 องศาเซลเซียส รูปร่างลักษณะขนาดองค์ประกอบธาตุและผลึกของ nanopowders ถูกตรวจสอบโดยการสแกนกล้องจุลทรรศน์อิเล็กตรอน (SEM, Hitachi, s-4800) กระจายพลังงานรังสี-x เปคโทรส (สหพันธ์) ที่แนบมากับ sem,การส่งผ่านกล้องจุลทรรศน์อิเล็กตรอน (Tem) แล​​ะ Tem ความละเอียดสูง (JEOL, jem-2010hr) ตามลำดับ ตัวอย่างสำหรับการสังเกต Tem ถูกจัดทำขึ้นโดยกระจายในเอทานอล ความแตกต่างความร้อนสแกน (dsc, Netzsch-Bruker,sta449f3jupiter-tensor27) การทดลองได้รับการดำเนินการโดยใช้ความร้อนของดูปองท์วิเคราะห์ความแตกต่างในการไหลเวียนของบรรยากาศในช่วง 25-120 องศาเซลเซียสมีอัตราการให้ความร้อนจาก 5 k-1 นาทีและในวัดที่สลับกระบวนการขั้นตอนการให้ความร้อนกับการระบายความร้อนรัฐม่านแขวนของวีตามที่ได้รับ 1 -