Abstract
Zeolite SAPO-34 was used for fabrication of mixed matrix membranes (MMMs) to improve the CO2/CH4/N2 gas separation performance of the neat Pebax1074 membrane. Permeability and selectivity of the MMMs were studied at different temperatures of 25–65 °C and pressures of 4–24 bars. Also sorption of different gases in MMMs was measured at 35 °C and different pressures, which showed enhanced solubility coefficients. Moreover, thermal, morphological and mechanical properties of MMMs were characterized by differential scanning calorimetry (DSC), scanning electron microscope (SEM) and tensile analysis. The results showed excellent improvement in CO2/CH4 selectivity (about 70%) and CO2/N2 selectivity (about 15%) at 20 wt% SAPO-34 loading.