In the test, a sample of 6–8 mg was placed on an alumina pan to alleviate
the problem caused by the diffusion resistance associated
with the adsorbent packing. Before adsorption, the sample was
purged with nitrogen (99.8%, 60 mL/min) and heated at 400 C
for 40 min to release the water and impurities adsorbed.