5.8.2 Frequency response of ZnO mat

5.8.2 Frequency response of ZnO material
Early measurements [39, 52, 114] on the frequency response of ZnO material ceramics
were achieved using a General Radio capacitance bridge, and because of the very
small size of the tested samples, the applied voltage was merely 1 V r.m.s. In the
frequency range 10–105 Hz, the calculated relative permittivity from capacitance
measurements is unexpectedly high (1000–1600) considering that the relative permittivity
for ZnO is in the range εr = 8 to 10, and for the additives is in the range
εr = 16 to 25. This can be partially accounted for by the microstructure of ZnO material.
As used in surge arresters, the material consists of ZnO grains (approximately25 μm) of high conductivity separated by a very thin layer (

ผลลัพธ์ (ไทย) 1:

5.8.2 ตอบสนองความถี่วัสดุ ZnO
ต้นวัด [39, 52, 114] ตอบสนองความถี่ของเครื่องเคลือบวัสดุ ZnO
สำเร็จใช้บริดจ์ความวิทยุทั่วไป และเนื่องจากมาก
ขนาดเล็กตัวอย่างทดสอบ แรงดันไฟฟ้าที่ใช้ได้เพียง 1 V r.m.s. ในการ
ความถี่ช่วง 10-105 Hz, permittivity สัมพัทธ์คำนวณได้จากค่าความจุ
วัดได้สูงโดยไม่คาดคิด (1000-1600) พิจารณาที่ permittivity ญาติ
สำหรับ ZnO เป็น εr ช่วง = 8-10 และสำหรับสารอยู่ในช่วง
εr = 16-25 นี้สามารถมีบางส่วนคิด โดยต่อโครงสร้างจุลภาคของวัสดุ ZnO ได้
ใช้ในกระแส arresters วัสดุประกอบด้วยเกรนของ ZnO (approximately25 μm) ของนำสูงคั่น ด้วยชั้นที่บางมาก (< 100 ล) สาร
ซึ่งควบคุมลักษณะที่ไม่ใช่เชิงเส้น ดังนั้น ความจริงเป็นฉนวนหนา

ผลลัพธ์ (ไทย) 2:

5.8.2 Frequency response of ZnO material
Early measurements [39, 52, 114] on the frequency response of ZnO material ceramics
were achieved using a General Radio capacitance bridge, and because of the very
small size of the tested samples, the applied voltage was merely 1 V r.m.s. In the
frequency range 10–105 Hz, the calculated relative permittivity from capacitance
measurements is unexpectedly high (1000–1600) considering that the relative permittivity
for ZnO is in the range εr = 8 to 10, and for the additives is in the range
εr = 16 to 25. This can be partially accounted for by the microstructure of ZnO material.
As used in surge arresters, the material consists of ZnO grains (approximately25 μm) of high conductivity separated by a very thin layer (<100 ล) of additives
which controls the non-linear characteristics. Therefore, the true dielectric thickness

ผลลัพธ์ (ไทย) 3:

5.8.2 การตอบสนองความถี่ของวัสดุก่อนการวัด [
P 39 , 52 , 114 ] ในการตอบสนองความถี่ของซิงค์ออกไซด์วัสดุเซรามิก
ยาโดยใช้วิทยุทั่วไปความจุสะพานและเพราะมาก
ขนาดเล็กของการทดสอบตัวอย่าง ความต่างศักย์เป็นเพียง 1 ใน r.m.s. ในช่วงความถี่ 10 Hz
– 105 , ญาติที่ป้อนค่า Capacitance
จากวัดสูงโดยไม่คาดคิด ( 1000 - 1600 ) พิจารณาว่า
ป้อนญาติซิงค์ออกไซด์อยู่ในช่วงε r = 8 ถึง 10 และวัตถุเจือปนอยู่ในช่วง
ε r = 16 25 นี่เป็นบางส่วนที่คิดโดยโครงสร้างจุลภาคของวัสดุที่ใช้ใน P .
กระแส arrestersวัสดุที่ประกอบด้วยซิงค์ออกไซด์เม็ด ( approximately25 μเมตร ) สูงนำโดยแยกเป็นชั้นบางมาก ( < 100 รูป ) วัตถุเจือปน
ซึ่งควบคุมลักษณะไม่เป็นเชิงเส้น ดังนั้น ทรู
หนาอิเล็กทริก