In this process, the CO2 gas forms a weak acid which hydrolyzes the sodium silicate, thus forming an amorphous silica that becomes the bond. There is also a bonding action from the sodium silicate itself. The use of CO2 gives an almost instantaneous set. The mold is fully hardened before the pattern is drawn from the mold sections.