Fig. 1 demonstrates cracks on the kernel surface at various degrees. At the 100% surface cracking degree, for example, the kernel sur- faces of KML and CHN are filled with a large number of short, deep red-violet lines. Lesser degrees of cracking were observed on the surface of the kernel, with the appearance of dark lines fewer in number and with a reduced color intensity.