These results are higher than those obtained at higher loads with traditional hardness
measurements (i.e. 49 mN or 1.96 N). Meanwhile, due to the small
size of the silver rich phase and the size of the indentations (about
400 nm), contribution of the second phase precipitation cannot be
clearly distinguished following NHT indentation.