The current-voltage (I-V) measurements were carried out with an active area of 0.16 cm2
by a Kiethley
2400 source meter, Kiethley 617 programable electrometer measured unit under AM 1.5 global simulated sunlight
(100 mW/cm2
) which was produce by a 500 W Oriel Solar Simulator (New Port BB-L, USA). The incident light
intensity was calibrated to 1 sun by a photovoltaic reference cell system (91150, Oriel instruments, USA).
Electrochemical impedance spectroscopy (EIS) was measured in 1 sun illumination in an open-circuit at 0.6 - 0.7 V
and with a frequency range from 105 to 101 Hz at an amplitude of 10 mV. The obtained spectra were fitted by ZIVE
ZMAN 2.2 software. Moreover, the gel electrolytes were also characterized by FT-IR, DSC and TGA.
The current-voltage (I-V) measurements were carried out with an active area of 0.16 cm2 by a Kiethley2400 source meter, Kiethley 617 programable electrometer measured unit under AM 1.5 global simulated sunlight(100 mW/cm2) which was produce by a 500 W Oriel Solar Simulator (New Port BB-L, USA). The incident light intensity was calibrated to 1 sun by a photovoltaic reference cell system (91150, Oriel instruments, USA).Electrochemical impedance spectroscopy (EIS) was measured in 1 sun illumination in an open-circuit at 0.6 - 0.7 Vand with a frequency range from 105 to 101 Hz at an amplitude of 10 mV. The obtained spectra were fitted by ZIVEZMAN 2.2 software. Moreover, the gel electrolytes were also characterized by FT-IR, DSC and TGA.