Tm of PLA blends was shifted to higher temperature compared to that of neat PLA. Moreover, degree of crystallinity (%XC) of PLA blends was lower than that of neat PLA
Tm of PLA blends wasshifted to higher temperature compared to that of neat PLA. Moreover, degree ofcrystallinity (%XC) of PLA blends was lower than that of neat PLA