For ferroelectric memory applications utilizing PZT, mostly Ti-rich compositions are used because of their large spontaneous polarization available, in accordance to Equation (1.16), and because the hysteresis loops of ferroelectric thin films are squarer for tetragonal than for rhombohedral compositions.