Their phase angle (d) values were
also comparable (p> 0.05, Table 1) from very low to high
frequencies (Fig. 1B). The strain-sweep profiles (Fig. 2) demonstrated
similar linear viscoelastic (LVE) ranges and G0eG00 cross-over
points (G0 ¼G00), indicating the strain sensitivity and transition
point from elastic to viscous behaviour were not affected by
homogenization condition.