It is of interest to note that crystalline polyethylene has a negative electron affinity, i.e. the bottom of the conduction band is approximately 1 eV above the vacuum level, and electron traps with depths in the range 0–0.3 eV formed by the conformations of the polymer chains themselves are to be expected in semi-crystalline
polyethylene [9–11].