JEOL Scanning Electron Microscope JSM 6390 LV was used. Morphologies were
obtained at a current and working distance of 15 kV and 9 mm respectively. Specimens
were coated with 10 nm platinum in an ‘Auto Fine Coater’ before positioning
against electron gun. Platinum coating was carried out at 20 mA for about 60 s.