The coloristic and the transparency

The coloristic and the transparency were measured
using a Minolta CM-3600d (gloss included) and the
calculation of L*, a*, b*, C*, h, DE* and DTransparency
with CGREC software according to DIN 6174. As
substrates for coloristics, Leneta black/white cardboard
was used. The gloss evaluation was performed with a Byk/Gardner Micro-Tri-Gloss meter according to DIN
67530. Cracking evaluation was performed visually
according the crack formation scale 353 from TNO
(Netherlands Organization for Applied Scientific
Research). Integrated transmittance spectra were
recorded on paint films (DFT = 70 lm on glass plates)
between 200 nm and 800 nm with 1 nm resolution using a
PerkinElmer Lambda 650 UV/VIS spectrophotometer.

ผลลัพธ์ (ไทย) 2:

coloristic
และความโปร่งใสถูกวัดโดยใช้Minolta CM-3600d (กลอสรวม)
และการคำนวณของL * a * b * * C, H, DE * และ DTransparency
กับซอฟต์แวร์ CGREC ตาม DIN 6174.
ขณะที่พื้นผิวสำหรับcoloristics, Leneta สีดำ /
กล่องกระดาษสีขาวถูกนำมาใช้ การประเมินความเงางามได้รับการดำเนินการกับ Byk / การ์ดเนอร์ไมโคร Tri-Gloss เมตรตามมาตรฐาน DIN
67530 การประเมินผลแตกได้ดำเนินการทางสายตาตามรูปแบบแตกขนาด 353 จาก TNO (เนเธอร์แลนด์องค์การเพื่อการประยุกต์ใช้วิทยาศาสตร์การวิจัย) สเปกตรัมการส่งผ่านแบบบูรณาการได้รับการบันทึกลงบนฟิล์มสี (DFT = 70 LM บนจานแก้ว) ระหว่าง 200 นาโนเมตรและ 800 นาโนเมตรที่มีความละเอียด 1 นาโนเมตรโดยใช้PerkinElmer แลมบ์ดา 650 UV / VIS spectrophotometer

ผลลัพธ์ (ไทย) 3:

การ coloristic และความโปร่งใสวัด
ใช้ Minolta cm-3600d ( เงารวม ) และการคำนวณ
L * a * b * C * h , * dtransparency
กับซอฟต์แวร์ cgrec ตาม DIN 6174 . เป็นจำนวน coloristics
,
leneta สีดำ / ขาวกระดาษแข็งที่ใช้ กลอสการประเมินแสดงกับ byk / การ์ดเนอร์ไมโครเมตรไตรเงาตาม DIN
67530 .การประเมินผลการปฏิบัติตามการมองเห็นรอยแตกเกิด

( องค์กร tno ขนาด 353 จากเนเธอร์แลนด์ สำหรับการวิจัยทางวิทยาศาสตร์
ประยุกต์ ) โดยการบูรณาการถูกบันทึกไว้ในฟิล์ม
สี ( DFT = 70 LM บนแผ่นแก้ว )
ระหว่าง 200 nm และ 800 nm 1 nm ละเอียดด้วย
Perkinelmer แลมบ์ดา ( UV / VIS วัสดุ