It was observed from the micrographs that the Y358 sample contains less porosity (P) and non-superconducting Cu, Ba-rich (Cu, Ba-r) phase detected by mapping from the EDS in despite of the fact that the average size of the superconducting grain of the Y358 sample becomes smaller in comparison with the other.