Vetter et al. [1] classified the growth defects in sputter-deposited
a-C films as through-voids, close voids, flake formation, overcoated
particles and those due to the coarse columnar morphology.
Flakes are generated when some foreign particles are at the
substrate surface before the coating starts to grow, or they are built
into the growing coating