Fig. 1. WAXD profiles (a) and DSC melting curves (b) of equimolar PLLA50/PDLA50 blends prepared by low temperature approach (at different processing temperatures lower than
220 °C), compared with conventional melt blending (at processing temperature of 220 °C) and solution casting.