The starting DSW material was tested with thermogravimetric analysis (TGA) equipment to investigate the composition of material as provided by our collaborator. Samples were heated from 300C up to 900 0C under a nitrogen atmosphere with the heating rate of 20 _C/min and the weight loss was recorded. Total four random samples between 4 and 7 mg were analyzed.