This project was conducted to produ

This project was conducted to produce a cement panel with the addition of treated and untreated coconut fiber in
cement panel. Coconut fiber was added to replace coarse aggregate (sand) in this cement panel. In this project, the
ratios used to design the mixture were 1:1:0, 1:0.97:0.03, 1:0.94:0.06, 1:0.91:0.09 (cement: sand: coconut fiber). The
water cement ratio was constant at 0.55. The sizes of sample tested were, 160 mm x 40 mm x 40 mm for compression
test, and 100 mm x 100 mm x 40 mm for density, moisture content and water absorption tests. After curing samples
for 28 days, it was found that the addition of coconut fiber, further increase in compressive strength of cement panel
with untreated coconut fiber. Moisture content of cement panel with treated coconut fiber increased with increasing
content of coconut fiber whereas water absorption of cement panel with untreated coconut fiber increased with
increasing content of coconut fiber. The density of cement panel decreased with the addition of untreated and treated
coconut fiber.

ผลลัพธ์ (ไทย) 3:

โครงการนี้มีวัตถุประสงค์เพื่อผลิตปูนซีเมนต์แผงด้วยนอกเหนือจากการรักษาและใยมะพร้าวดิบใน
ซีเมนต์แผง ใยมะพร้าวที่ถูกเพิ่มเข้ามาเพื่อแทนที่มวลรวมหยาบ ( ทราย ) ในแผงปูนนี้ ในโครงการนี้ เพื่อออกแบบ
อัตราส่วนที่ใช้ผสมเป็น 1:1:0 1:0.97: 0.03 , 0.06 , 1:0.94: 1:0.91: 0.09 , ปูนซีเมนต์ : ทราย : ขุยมะพร้าวใย )
อัตราส่วนน้ำซีเมนต์คงที่เท่ากับ 0.55 .ขนาดของตัวอย่างทดสอบ , 160 มม. x 40 มม. x 40 มม. เพื่อทดสอบแรงอัด
, และ 100 มม. x 100 มม. x 40 มม. สำหรับความหนาแน่นและความชื้นและน้ำการทดสอบการดูดซึม หลังจากบ่มตัวอย่าง
เป็นเวลา 28 วัน พบว่า นอกจากใยมะพร้าว ต่อไปเพิ่มกำลังอัดของซีเมนต์แผง
ด้วยใยมะพร้าวดิบความชื้นของปูนด้วยแผงทำใยมะพร้าวเพิ่มขึ้น
เนื้อหาของใยมะพร้าวและการดูดซึมน้ำของซีเมนต์ด้วยแผงใยมะพร้าวดิบเพิ่มขึ้น
เพิ่มปริมาณของใยมะพร้าว ความหนาแน่นของแผงซีเมนต์ลดลง ด้วยการเพิ่มสารและปฏิบัติ
ใยมะพร้าว