4. Conclusions
The present results indicate that the radiation-cured
formulations of SBR containing45 phr of HAF-carbon
black, 1.5 phr of coagent SR-633, 1 phr of both IPPD
and TMQ, 5 phr of EPDM and irradiated to 150 kGy
have superior mechanical properties and thermal stability
compared with those of the chemically vulcanized
compounds. Whereas, the radiation-cured formulations
of the NR rubber formulation containing45 phr of
HAF-carbon black, 5 phr of the coagent 517, 1 phr of
IPPD, 1 phr of TMQ, 1 phr of paraffin wax and
irradiated to 200 kGy have similar mechanical properties
but superior thermal stability (based on the % change in
E after thermal aging), when compared with those of the
sulfur-vulcanized compounds and slightly better than
those of the peroxide-vulcanized compounds.
4. บทสรุปผลลัพธ์ปัจจุบันบ่งชี้ว่า การฉายรังสีรักษาสูตร phr containing45 SBR ของคาร์บอน HAFสีดำ phr 1.5 ของ coagent SR-633, phr 1 ของ IPPD ทั้งและ TMQ, phr 5 ของ EPDM และ irradiated ไป 150 kGyมีคุณสมบัติเหนือกว่าเครื่องจักรกลและเสถียรภาพความร้อนเทียบกับที่สารเคมี vulcanized รองเท้าถสารประกอบ ในขณะที่ สูตรรักษารังสีของ NR ยางกำหนด containing45 phr ของHAF คาร์บอนดำ phr 5 ของ coagent 517, phr 1 ของIPPD, phr 1 ของ TMQ, phr 1 ของพาราฟิน และirradiated ไป 200 kGy มีคุณสมบัติคล้ายเครื่องจักรกลแต่เหนือกว่าเสถียรภาพความร้อน (ขึ้นอยู่กับการเปลี่ยนแปลง%E หลังจากอายุความร้อน), เมื่อเทียบกับการสารประกอบกำมะถัน vulcanized รองเท้าถ และเล็กน้อยดีกว่าผู้สารเพอร์ออกไซด์ vulcanized รองเท้าถ