Neither their
migrations nor their annihilations were observed. This result is
consistent with the previous observation [51] that vacancy clusters
in copper were thermally immobile below 110 K. Since our simulations
were conducted at 0 K, the thermal barrier for vacancy migration
could not be overcome.