At room temperature, the more brittle, densely fired refractories have work-of-fracture values of about 30 J/m2 and the microstructurally well-designed refractories have work-of-fracture values of about 100 J/m2, or more. It should be apparent that refractories are substantially more resistant to crack growth than to crack initiation, by a factor of 10 or more