While trying to improve the surface quality of milled surfaces, it is evident that PWJ milling using a jet traverse speed of 250 mm/min in one pass is energetic enough to erode a significant volume of the clad surface (Fig. 7), and subsequent milling passes done by employing a higher jet traverse speed would result in a lower erosion rate of the material.