The increase in the corrosion rate of hightemperature
aged alloy N06022 is pronounced
in highly reducing conditions (boiling pure HCl
solutions) and highly oxidizing solutions (boiling
50% H2SO4 plus 42 g/L Fe2(SO4)3. However,
at intermediate oxidizing potentials, the
aged alloy is still able to maintain passivity.