The results showed that increasing citric acid content led to an increase in crosslinking degree which enhanced the physical strength of the hydrogels. Water absorbency, as indicated by swelling ratio, of hydrogels initially increased with increasing citric acid content, reached maximum at the optimal concentration and declined at higher concentratio